| Specifications |
| Gloss
@ 60 degree Angle: |
High
Gloss Up to 85 degrees |
| Weight
Gallon: |
8.4
lbs./gallon kit (Combined Parts A, B, & C) |
| Catalyze
Ratio: |
As
supplied in pre-measured kit |
| Weight
Solids: |
45%
+ or - 3% Catalyzed & Reduced |
| Volume
Solids: |
41%
+ or - 3% Catalyzed & Reduced |
| Freeze
Thaw Stability: |
3
cycles |
| Flashpoint: |
>
200 degress F |
| VOC's: |
Parts
A + B + C: 67 grams/liter |
| Adhesion
(ASTM D3359): |
Ave.
results 5B (0% removed) |
| Humidity
(ASTM D2247): |
Minimal
change at 1,500 hrs |
| Abrasion
(ASTM D4060): |
Ave.
of 725 cycles to wear throughout |
| Hardness
(ASTM D3363): |
Gouge:
3H-HB;Scratch 2B-4B |
Impact
Resistance
(ASTM D2794): |
18.6
in-lbs. |
| Flexibility
(ASTM D522): |
Cracking
res.:< 1/8" |
Elongation,
%
(ASTM 522): |
>
33.6% |
Xenon
Arc Weathering
(G115) @ 1,500hrs::
|
No
measurable gloss loss or yellowing |
|
MEK
- double rubs:
|
100
double rubs |
|
Application
Viscosity:
|
65-75
KU Catalyzed & reduced |
| Application
Conditions: |
Up
to 80% Relative Humidity, 40 - 95 degrees F Air & Surface
Temperature. |
| Recommended
Film Thickness: |
Wet:
5 - 6 mils: Dry: 2.5 - 3 mils |
| Actual
Spread Rate: |
350
- 450 sq ft per gallon |
| Pot
Life: |
1.5
hours |
| Recommended
Coats: |
One
or two, depends on performance requirements and substrate
profile |
| Clean-up: |
Water
or you may use a mixture of water and a small amount of
ammonia |
Air
Dry Schedule @
75 degrees F, 50% humidity: |
Recoat/Handle:
8 hours - After 7 days scuff sanding may be required. Full
Cure 7 days @ 75 degrees F, 50% RH |
Wet
Standard Coefficient
of Friction (COF): |
.86
Average |